A Microporous Copper Metal–Organic Framework with High H 2 and CO 2 Adsorption Capacity at Ambient Pressure

Author(s) -

Lässig Daniel,

Lincke Jörg,

Moellmer Jens,

Reichenbach Christian,

Moeller Andreas,

Gläser Roger,

Kalies Grit,

Cychosz Katie A.,

Thommes Matthias,

Staudt Reiner,

Krautscheid Harald

Publication year - 2011

Publication title -

angewandte chemie

Language(s) - German

Resource type - Journals

eISSN - 1521-3757

pISSN - 0044-8249

DOI - 10.1002/ange.201102329

Subject(s) - microporous material , metal organic framework , copper , adsorption , chemistry , metal , high pressure , polymer chemistry , inorganic chemistry , organic chemistry , physics , thermodynamics

Voll aufnahmebereit : Aufnahmen von 9.2 mmol g −1 (40.5 Gew.‐%) für CO 2 bei 273 K/0.1 MPa und 15.23 mmol g −1 (3.07 Gew.‐%) für H 2 bei 77 K/0.1 MPa zählen zu den höchsten bekannten Werten für Metall‐organische Gerüste (MOFs). Gefunden wurden sie für ein neuartiges, hoch mikroporöses Kupfer‐MOF (siehe Bild; Cu türkis, O rot, N blau). Thermische Analysen zeigen eine Stabilität des flexiblen Gerüsts bis 250 °C.