3D Cube‐Maze‐Like Li‐Rich Layered Cathodes Assembled from 2D Porous Nanosheets for Enhanced Cycle Stability and Rate Capability of Lithium‐Ion Batteries
Author(s) -
Liu Yanchen,
Wang Jing,
Wu Junwei,
Ding Zhiyu,
Yao Penghui,
Zhang Sanli,
Chen Yanan
Publication year - 2020
Publication title -
advanced energy materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 10.08
H-Index - 220
eISSN - 1614-6840
pISSN - 1614-6832
DOI - 10.1002/aenm.201903139
Subject(s) - materials science , anode , cathode , lithium (medication) , chemical engineering , graphite , hydrothermal circulation , porosity , oxide , nanotechnology , cube (algebra) , mesoporous material , ion , composite material , electrode , catalysis , electrical engineering , organic chemistry , medicine , chemistry , mathematics , combinatorics , endocrinology , metallurgy , engineering
Li‐rich oxide is a promising candidate for the cathodes of next‐generation lithium‐ion batteries. However, its utilization is restricted by cycling instability and inferior rate capability. To tackle these issues, three‐dimensional (3D), hierarchical, cube‐maze‐like Li‐rich cathodes assembled from two‐dimensional (2D), thin nanosheets with exposed {010} active planes, are developed by a facile hydrothermal approach. Benefiting from their unique architecture, 3D cube‐maze‐like cathodes demonstrate a superior reversible capacity (285.3 mAh g −1 at 0.1 C, 133.4 mAh g −1 at 20.0 C) and a great cycle stability (capacity retention of 87.4% after 400 cycles at 2.0 C, 85.2% after 600 cycles and 75.0% after 1200 cycles at 20.0 C). When this material is matched with a graphite anode, the full cell achieves a remarkable discharge capacity (275.2 mAh g −1 at 0.1 C) and stable cycling behavior (capacity retention of 88.7% after 100 cycles at 5.0 C, capacity retention of 84.8% after 100 cycles at 20.0 C). The present work proposes an accessible way to construct 3D hierarchical architecture assembled from 2D nanosheets with exposed high‐energy active {010} planes and verifies its validity for advanced Li‐rich cathodes.