Structural, Spectroscopic, and Excitonic Dynamic Characterization in Atomically Thin Yb 3+ ‐Doped MoS 2 , Fabricated by Femtosecond Pulsed Laser Deposition
Author(s) -
Maddi Chiranjeevi,
Aswin Jyothilakshmi Ravi,
Scott Andrew,
Aslam Zabeada,
Willneff Elizabeth,
Adarsh Kumaran Nair Vasala Devi,
Jha Animesh
Publication year - 2019
Publication title -
advanced optical materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 2.89
H-Index - 91
ISSN - 2195-1071
DOI - 10.1002/adom.201900753
Subject(s) - materials science , x ray photoelectron spectroscopy , raman spectroscopy , femtosecond , doping , thin film , photoluminescence , pulsed laser deposition , analytical chemistry (journal) , exciton , spectroscopy , optoelectronics , dopant , ultrafast laser spectroscopy , laser , absorption spectroscopy , nanotechnology , optics , nuclear magnetic resonance , chemistry , physics , chromatography , quantum mechanics
The large area deposition and synthesis of 10 mm × 10 mm atomically thin Yb 3+ ‐doped MoS 2 films by femtosecond pulsed laser deposition on a silica glass optical platform for device applications are demonstrated for the first time. The presence of Yb 3+ ‐ion doping is confirmed using photoluminescence (PL), X‐ray photoelectron spectroscopy (XPS), and Raman spectroscopy. The Yb 3+ ‐doped MoS 2 films, when excited with a 976 nm laser, exhibit room temperature PL with a peak at 1002 nm. The XPS and Raman spectroscopic analyses of the Yb 3+ ‐doped and undoped films show that the deposited films are a mixture of 2H‐ and 1T‐MoS 2 after postdeposition annealing at 500 °C. The density functional theory analysis shows that the 1T phase is metastable by +77 kJ (≈0.8 eV) mol ‐1 , when compared with the 2H state at 0 K. Ultrafast transient nonlinear optical spectroscopic measurements prove that the saturable absorption of undoped MoS 2 is significantly modified after Yb 3+ ‐ion doping, by displaying dopant‐host structure charge transfer. The complex transient absorption line shape shows a combination of bleach (negative) signals at the A (670 nm) and B (630 nm) exciton energies, and a strong induced absorption below the A exciton level. The results presented herein provide critical insight in designing novel rare‐earth‐ion doped 2D materials and devices.