Nano‐Twisted Double Helix Carbon Debris Improves the Wear Resistance of Ultra‐Thick Diamond‐Like Carbon Coatings
Author(s) -
Sui Xudong,
Wang Xinyu,
Zhang Shuaituo,
Yan Mingming,
Li Wensheng,
Hao Junying,
Liu Weimin
Publication year - 2020
Publication title -
advanced materials interfaces
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 1.671
H-Index - 65
ISSN - 2196-7350
DOI - 10.1002/admi.202000857
Subject(s) - materials science , coating , tribology , composite material , diamond like carbon , carbon fibers , layer (electronics) , silicon , nano , metallurgy , nanotechnology , thin film , composite number
Thick diamond‐like carbon (DLC) coatings with different silicon (Si) transition layer thickness are deposited by hollow cathode plasma immersion coating technology. The results show that the internal stress of the coating can be tuned by changing the deposition time of Si transition layer, thereby obtaining good adhesion strength. Friction and wear results show that all coatings have good tribological properties. The coating with 8 min Si transition layer (Si‐8) demonstrates the lowest friction coefficient (μ ≈ 0.03), even achieves ultralow friction (μ ≈ 0.008) for a short time. However, the wear rate of Si‐8 coating is found to be the largest (2.1 × 10 −16 m 3 (N m) −1 . The low friction coefficient of Si‐8 coating is related to its high degree of graphitization, complete transfer film and fine wear debris. In contrast, the Si‐16 coating has the lowest wear rate of about 5.6 × 10 −17 m 3 (N m) −1 with a relatively high friction coefficient (μ ≈ 0.1). This is due to its high hardness and the formation of a nano‐twisted double helix carbon debris during the friction process. This nano‐twisted double helix structure can consume additional plastic deformation energy, while reducing the interface contact area and increasing the interface bearing capacity, thereby improving the wear resistance of the thick DLC coating.