Atomic Sulfur Covalently Engineered Interlayers of Ti 3 C 2 MXene for Ultra‐Fast Sodium‐Ion Storage by Enhanced Pseudocapacitance
Author(s) -
Luo Jianmin,
Zheng Jianhui,
Nai Jianwei,
Jin Chengbin,
Yuan Huadong,
Sheng Ouwei,
Liu Yujing,
Fang Ruyi,
Zhang Wenkui,
Huang Hui,
Gan Yongping,
Xia Yang,
Liang Chu,
Zhang Jun,
Li Weiyang,
Tao Xinyong
Publication year - 2019
Publication title -
advanced functional materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 6.069
H-Index - 322
eISSN - 1616-3028
pISSN - 1616-301X
DOI - 10.1002/adfm.201808107
Subject(s) - pseudocapacitance , materials science , mxenes , anode , sodium ion battery , electrochemistry , chemical engineering , energy storage , cathode , ion , electrode , nanotechnology , supercapacitor , chemistry , engineering , power (physics) , physics , faraday efficiency , quantum mechanics
2D MXenes have been widely applied in the field of electrochemical energy storage owning to their high electrical conductivity and large redox‐active surface area. However, electrodes made from multilayered MXene with small interlayer spacing exhibit sluggish kinetics with low capacity for sodium‐ion storage. Herein, Ti 3 C 2 MXene with expanded and engineered interlayer spacing for excellent storage capability is demonstrated. After cetyltrimethylammonium bromide pretreatment, S atoms are successfully intercalated into the interlayer of Ti 3 C 2 to form a desirable interlayer‐expanded structure via TiS bonding, while pristine Ti 3 C 2 is hardly to be intercalated. When the annealing temperature is 450 °C, the S atoms intercalated Ti 3 C 2 (CT‐S@Ti 3 C 2 ‐450) electrode delivers the improved Na‐ion capacity of 550 mAh g −1 at 0.1 A g −1 (≈120 mAh g −1 at 15 A g −1 , the best MXene‐based Na + ‐storage rate performance reported so far), and excellent cycling stability over 5000 cycles at 10 A g −1 by enhanced pseudocapacitance. The enhanced sodium‐ion storage capability has also been verified by theoretical calculations and kinetic analysis. Coupling the CT‐S@Ti 3 C 2 ‐450 anode with commercial AC cathode, the assembled Na + capacitor delivers high energy density (263.2 Wh kg −1 ) under high power density (8240 W kg −1 ), and outstanding cycling performance.