Unraveling the Effect of Conformational and Electronic Disorder in the Charge Transport Processes of Semiconducting Polymers
Author(s) -
Chew Annabel R.,
Ghosh Raja,
Pakhnyuk Viktoria,
Onorato Jonathan,
Davidson Emily C.,
Segalman Rachel A.,
Luscombe Christine K.,
Spano Frank C.,
Salleo Alberto
Publication year - 2018
Publication title -
advanced functional materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 6.069
H-Index - 322
eISSN - 1616-3028
pISSN - 1616-301X
DOI - 10.1002/adfm.201804142
Subject(s) - delocalized electron , polaron , materials science , chemical physics , polymer , characterization (materials science) , nanoscopic scale , charge carrier , nanotechnology , chemistry , physics , optoelectronics , organic chemistry , quantum mechanics , composite material , electron
Charge transport in semiconducting polymers is inextricably linked to their microstructure, making the characterization of polymer morphology at all length‐scales essential for understanding the factors that limit mobility in these materials. Indeed, charge transport depends both on the ability of polarons to delocalize at the approximately nanometer length‐scale and navigate a complex energetic and morphological mesoscale landscape. While characterization of the mesoscale morphology of polymers is well‐established, studies of the local chain packing and nanoscale disorder, which affect delocalization, can be significantly more difficult to carry out. Through infrared charge modulation spectroscopy and theoretical modeling, the effect of the local chain environment on polaron delocalization is directly measured and quantified. Using a series of polymers based on the model system, poly(3‐hexylthiophene), the link between disorder and polaron localization is systematically explored. Polaron delocalization is correlated with known trends in mobility, revealing that while charge delocalization is always beneficial, the formation of tie‐chains is necessary to reach the highest mobilities in semicrystalline polymers. The results provide direct evidence for the importance of both nanoscale (charge carrier delocalization) and mesoscale (tie‐chains) orders, demonstrating the need to distinguish the key length‐scale limiting charge transport in the design of new, high mobility polymers.