Bendable Solar Cells from Stable, Flexible, and Transparent Conducting Electrodes Fabricated Using a Nitrogen‐Doped Ultrathin Copper Film
Author(s) -
Zhao Guoqing,
Kim Soo Min,
Lee SangGeul,
Bae TaeSung,
Mun ChaeWon,
Lee Sunghun,
Yu Huashun,
Lee GunHwan,
Lee HaeSeok,
Song Myungkwan,
Yun Jungheum
Publication year - 2016
Publication title -
advanced functional materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 6.069
H-Index - 322
eISSN - 1616-3028
pISSN - 1616-301X
DOI - 10.1002/adfm.201600392
Subject(s) - materials science , copper , sheet resistance , electrode , transmittance , indium tin oxide , solar cell , optoelectronics , doping , transparent conducting film , sputtering , indium , organic solar cell , zinc , nanotechnology , layer (electronics) , composite material , thin film , metallurgy , chemistry , polymer
Copper has attracted significant interests as an abundant and low‐cost alternative material for flexible transparent conducting electrodes (FTCEs). However, Cu‐based FTCEs still present unsolved technical issues, such as their inferior light transmittance and oxidation durability compared to conventional indium tin oxide (ITO) and silver metal electrodes. This study reports a novel technique for fabricating highly efficient FTCEs composed of a copper ultrathin film sandwiched between zinc oxides, with enhanced transparency and antioxidation performances. A completely continuous and smooth copper ultrathin film is fabricated by a simple room‐temperature reactive sputtering process involving controlled nitrogen doping (<1%) due to a dramatic improvement in the wettability of copper on zinc oxide surfaces. The electrode based on the nitrogen‐doped copper film exhibits an optimized average transmittance of 84% over a spectral range of 380 −1000 nm and a sheet resistance lower than 20 Ω sq −1 , with no electrical degradation after exposure to strong oxidation conditions for 760 h. Remarkably, a flexible organic solar cell based on the present Cu‐based FTCE achieves a power conversion efficiency of 7.1%, clearly exceeding that (6.6%) of solar cells utilizing the conventional ITO film, and this excellent performance is maintained even in almost completely bent configurations.