Direct Transfer Printing with Metal Oxide Layers for Fabricating Flexible Nanowire Devices
Author(s) -
Lee Sang Hoon,
Lee Tae Il,
Ham MoonHo,
Lee Su Jeong,
Park Ji Hyeon,
Kim Yun Cheol,
Biswas Pranab,
Myoung Jae Min
Publication year - 2015
Publication title -
advanced functional materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 6.069
H-Index - 322
eISSN - 1616-3028
pISSN - 1616-301X
DOI - 10.1002/adfm.201503502
Subject(s) - materials science , polydimethylsiloxane , transfer printing , photolithography , nanowire , layer (electronics) , oxide , polyimide , electrode , substrate (aquarium) , nanotechnology , metal , field effect transistor , optoelectronics , transistor , composite material , electrical engineering , metallurgy , chemistry , oceanography , engineering , voltage , geology
A direct printing method for fabricating devices by using metal oxide transfer layers instead of conventional transfer media such as polydimethylsiloxane is presented. Metal oxides are not damaged by organic solvents; therefore, electrodes with gaps less than 2 μm can be defined on a metal oxide transfer layer through photolithography. In order to determine a suitable metal oxide for use as transfer layer, the surface energies of various metal oxides are measured, and Au layers deposited on these oxides are transferred onto polyvinylphenol (PVP). To verify the feasibility of our approach, Au source–drain electrodes on transfer layers and Si nanowires (NWs) addressed by the dielectrophoretic (DEP) alignment process are transferred onto rigid and flexible PVP‐coated substrates. Based on transfer test and DEP process, Al 2 O 3 is determined to be the best transfer layer. Finally, Si NWs field effect transistors (FETs) are fabricated on a rigid Si substrate and a flexible polyimide film. As the channel length decreases from 3.442 to 1.767 μm, the mobility of FET on the Si substrate increases from 127.61 ± 37.64 to 181.60 ± 23.73 cm 2 V −1 s −1 . Furthermore, the flexible Si NWs FETs fabricated through this process show enhanced electrical properties with an increasing number of bending cycles.