Correlating Structure with Function in Thermally Annealed PCDTBT:PC 70 BM Photovoltaic Blends
Author(s) -
Wang Tao,
Pearson Andrew J.,
Dunbar Alan D. F.,
Staniec Paul A.,
Watters Darren C.,
Yi Hunan,
Ryan Anthony J.,
Jones Richard A. L.,
Iraqi Ahmed,
Lidzey David G.
Publication year - 2012
Publication title -
advanced functional materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 6.069
H-Index - 322
eISSN - 1616-3028
pISSN - 1616-301X
DOI - 10.1002/adfm.201102510
Subject(s) - materials science , annealing (glass) , glass transition , stacking , chemical engineering , fullerene , polymer , polymer blend , polymer solar cell , analytical chemistry (journal) , composite material , organic chemistry , copolymer , chemistry , engineering
A range of optical probes are used to study the nanoscale‐structure and electronic‐functionality of a photovoltaic‐applicable blend of the carbazole co‐polymer poly[ N ‐9′‐heptadecanyl‐2,7‐carbazole‐alt‐5,5‐(4′,7′‐di‐2‐thienyl‐2′,1′,3′‐benzothiadiazole) (PCDTBT) and the electronic accepting fullerene derivative (6,6)‐phenyl C 70 ‐butyric acid methyl ester (PC 70 BM). In particular, it is shown that the glass transition temperature of a PCDTBT:PC 70 BM blend thin‐film is not sensitive to the relative blend‐ratio or film thickness (at 1:4 blending ratio), but is sensitive to casting solvent and the type of substrate on which it is deposited. It is found that the glass transition temperature of the blend reduces on annealing; an observation consistent with disruption of π – π stacking between PCDTBT molecules. Reduced π – π stacking is correlated with reduced hole‐mobility in thermally annealed films. It is suggested that this explains the failure of such annealing protocols to substantially improve device‐efficiency. The annealing studies demonstrate that the blend only undergoes coarse phase‐separation when annealed at or above 155 °C, suggesting a promising degree of morphological stability of PCDTBT:PC 70 BM blends.