“Solvent Annealing” Effect in Polymer Solar Cells Based on Poly(3‐hexylthiophene) and Methanofullerenes
Author(s) -
Li G.,
Yao Y.,
Yang H.,
Shrotriya V.,
Yang G.,
Yang Y.
Publication year - 2007
Publication title -
advanced functional materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 6.069
H-Index - 322
eISSN - 1616-3028
pISSN - 1616-301X
DOI - 10.1002/adfm.200600624
Subject(s) - materials science , energy conversion efficiency , annealing (glass) , spin coating , polymer , solvent , photoluminescence , solar cell , short circuit , conjugated system , polymer solar cell , spectroscopy , absorption spectroscopy , chemical engineering , analytical chemistry (journal) , thin film , optoelectronics , organic chemistry , nanotechnology , optics , composite material , chemistry , physics , engineering , quantum mechanics , voltage
The self‐organization of the polymer in solar cells based on regioregular poly(3‐hexylthiophene) (RR‐P3HT):[6,6]‐phenyl C 61 ‐butyric acid methyl ester (PCBM) is studied systematically as a function of the spin‐coating time t s (varied from 20–80 s), which controls the solvent annealing time t a , the time taken by the solvent to dry after the spin‐coating process. These blend films are characterized by photoluminescence spectroscopy, UV‐vis absorption spectroscopy, atomic force microscopy, and grazing incidence X‐ray diffraction (GIXRD) measurements. The results indicate that the π‐conjugated structure of RR‐P3HT in the films is optimally developed when t a is greater than 1 min ( t s ∼ 50 s). For t s < 50 s, both the short‐circuit current ( J SC ) and the power conversion efficiency (PCE) of the corresponding polymer solar cells show a plateau region, whereas for 50 < t s < 55 s, the J SC and PCE values are significantly decreased, suggesting that there is a major change in the ordering of the polymer in this time window. The PCE decreases from 3.6 % for a film with a highly ordered π‐conjugated structure of RR‐P3HT to 1.2 % for a less‐ordered film. GIXRD results confirm the change in the ordering of the polymer. In particular, the incident photon‐to‐electron conversion efficiency spectrum of the less‐ordered solar cell shows a clear loss in both the overall magnitude and the long‐wavelength response. The solvent annealing effect is also studied for devices with different concentrations of PCBM (PCBM concentrations ranging from 25 to 67 wt %). Under “solvent annealing” conditions, the polymer is seen to be ordered even at 67 wt % PCBM loading. The open‐circuit voltage ( V OC ) is also affected by the ordering of the polymer and the PCBM loading in the active layer.