In vitro Evaluation of Tribocorrosion Induced Failure Mechanisms at the Cell‐Metal Interface for the Hip Implant Application
Author(s) -
Runa Maria,
Jenny Lau Eiklang,
Takoudis Christos,
Sukotjo Cortino,
Shokuhfar Tolou,
Rocha Luis,
Mathew Mathew
Publication year - 2017
Publication title -
advanced engineering materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.938
H-Index - 114
eISSN - 1527-2648
pISSN - 1438-1656
DOI - 10.1002/adem.201600797
Subject(s) - tribocorrosion , materials science , corrosion , passivation , tribology , metallurgy , cathodic protection , oxide , implant , metal , titanium alloy , electrochemistry , alloy , composite material , layer (electronics) , chemistry , surgery , medicine , electrode
In a hip joint environment, the bone‐metal implant interface of an implant is exposed to the combined effect of wear and corrosion (tribocorrosion). This may create mechanical instability and cause early failure of the implants. The aim of this work was to investigate the tribocorrosion behavior of Ti6Al4V alloys in the presence of bone‐forming cells cultured on its surface (cell‐metal interface), using an electrochemical and tribological approach. The results showed that at a cathodic potential (−0.9 V), the presence of osteoblast‐like cells and serum proteins in the media might induce a higher passivation rate of the oxide film, enhancing the corrosion resistance. However, when the surface is in steady state (0.7 V) they show a lower resistant to corrosion, increasing the susceptibility to corrosion.