Paper‐Derived Bioactive Glass Tape
Author(s) -
Stares Steferson Luiz,
Kirilenko Alina,
Fredel Márcio Celso,
Greil Peter,
Wondraczek Lothar,
Travitzky Nahum
Publication year - 2013
Publication title -
advanced engineering materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.938
H-Index - 114
eISSN - 1527-2648
pISSN - 1438-1656
DOI - 10.1002/adem.201200192
Subject(s) - materials science , composite material , porosity , microstructure , shrinkage , ceramic , glass fiber , flexural strength , modulus
Porous bioactive glass (BaG) structures were manufactured applying novel preceramic paper process. Preceramic papers were produced for aqueous suspensions loaded with different contents of pulp fiber and BaG filler. Pressure loading was applied in order to increase the packing density in the paper sheets. The paper sheets were sintered at 630 °C for 1 h. The porous glass–ceramic specimens were characterized for density, porosity, composition, microstructure, and mechanical properties. A pronounced volumetric shrinkage was observed, but no surface flaws or inhomogeneous areas were detected. The mechanical strength using the ball on three balls test and elastic modulus of sintered specimens vary between 21 and 33 MPa and 0.30–0.85 GPa, respectively.