Pervaporation Separation of Benzene/Cyclohexane Mixtures by Poly(vinyl chloride) Membranes
Author(s) -
Yildirim A. E.,
Hilmioglu N. D.,
Tulbentci S.
Publication year - 2001
Publication title -
chemical engineering and technology
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.403
H-Index - 81
eISSN - 1521-4125
pISSN - 0930-7516
DOI - 10.1002/1521-4125(200103)24:3<275::aid-ceat275>3.0.co;2-0
Subject(s) - pervaporation , cyclohexane , membrane , selectivity , sorption , vinyl chloride , benzene , polymer , permeation , chemical engineering , chemistry , polyvinyl chloride , polymer chemistry , chromatography , materials science , organic chemistry , copolymer , catalysis , biochemistry , engineering , adsorption
Sorption and pervaporation of benzene/cyclohexane mixtures were studied by using poly(vinyl chloride) (PVC) polymer. The effects of composition of benzene/cyclohexane mixture and temperature on sorption and pervaporation characteristics were determined at 30, 40, and 50 °C for the membranes containing 8 wt% PVC polymer. Liquid feed composition effects on the flux and the selectivity were determined for two different membranes at 30 °C. The membranes that were prepared from the solutions containing 4 wt% and 8 wt% PVC polymer have thicknesses of 30 μm and 50 μm, respectively. Membrane thickness changes with polymer content as expected. Total sorption increased with increasing concentration of benzene. Increasing the concentration of benzene resulted in increasing flux as well as decreasing selectivity also. Fluxes were increased and selectivity decreased with increasing temperature. The selectivity was not affected significantly with varying amounts of polymer in the casting solution but the flux decreased with increasing amount of polymer in the casting solution.