Role of interfacial potential in coagulation of cuprammonium cellulose solution
Author(s) -
Fushimi Fumiyoshi,
Watanabe Tetsuo,
Hiyoshi Tatsuo,
Yamashita Yasuhiko,
Osakai Toshiyuki
Publication year - 1996
Publication title -
journal of applied polymer science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.575
H-Index - 166
eISSN - 1097-4628
pISSN - 0021-8995
DOI - 10.1002/(sici)1097-4628(19960103)59:1<15::aid-app3>3.0.co;2-p
Subject(s) - electrolyte , flux (metallurgy) , coagulation , ammonia , diffusion , chemistry , ion , cellulose , chemical engineering , membrane , inorganic chemistry , analytical chemistry (journal) , chromatography , thermodynamics , electrode , organic chemistry , psychology , biochemistry , physics , psychiatry , engineering
The electric potential, copper ion flux, and ammonia flux across the interface of cuprammonium cellulose solution (CCS) and various 1.0 equiv/Lelectrolyte solutions (ES) at 25°C were measured. The interfacial potentials were strongly negative (–10 to –35 mV) with H 2 SO 4, HCI, and (NH 4 ) 2 SO 4 as ES, weakly positive (6 to 8 mV) with NaCl, KCl, LiCl, CsCL, and RbCl as ES, and strongly positive (19 to 34 mV) with KOH and NaOH as ES, generally showing values similar to the diffusion potentials for electrolyte solutions comprising ions of the same absolute charge. The ammonia flux (about 1 X 10 ‐4 mol/cm 2 /s) was relatively unaffected by the interfacial potential, but the copper ion flux was clearly dependent on it. These results, together with the observed rates of CCS coagulation, indicate that the mechanism of the coagulation was largely determined by the interfacial potential, with strongly negative potential gradients accelerating the Cu 2+ flux into the ES and CCS coagulation proceeding rapidly by Cu 2+ removal, strongly positive potential gradients accelerating the Na + flux into the CCS and coagulation proceeding rapidly via the formation of cellulose‐Na + complex, and the absence of a strong potential gradient capable of accelerating the ion flux resulting in slow coagulation by ammonia removal. It may therefore be possible to control the interfacial potential and the ion flux by the ES composition, and thus to influence the structure of regenerated cellulosic fibers and membranes. © 1996 John Wiley & Sons, Inc.