Breaking the Upper Limit of Substitution Concentration in Li Argyrodite Solid Electrolytes Using a Single‐Solvent‐Mediated Approach
Author(s) -
Choi Ji Woong,
Kim WoongJu,
Hwang SukHo,
Kim SungChul,
Shin Yoonju,
Ahn Sangdoo,
Lee Young Joo,
Kang Jin Gu,
Kim DongWan
Publication year - 2025
Publication title -
advanced energy materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 10.08
H-Index - 220
eISSN - 1614-6840
pISSN - 1614-6832
DOI - 10.1002/aenm.202500532
Subject(s) - materials science , electrolyte , limit (mathematics) , solvent , substitution (logic) , fast ion conductor , inorganic chemistry , chemical engineering , chemistry , electrode , organic chemistry , mathematical analysis , mathematics , computer science , engineering , programming language
Abstract Although raising the substitution concentration of aliovalent cations in Li argyrodite solid electrolytes could boost solid‐state battery performance, surpassing the known substitution limit has not been attempted. In this study, the upper substitution limit of a Li 6+x P 1−x Si x S 5 Br solid electrolyte is increased using a single‐solvent‐mediated approach. The limit attained through this method is ≈40%, whereas that achieved through solid‐state ball milling is ≈30%. This result is validated by monitoring variations in the interplanar distance, Raman shift, and ionic conductivity with respect to the substitution level. The ionic conductivity of Li 6.4 P 0.6 Si 0.4 S 5 Br is as high as ≈3.1 mS cm −1 , exceeding that accomplished through ball milling. The enhanced limit is ascribed to the reduced particle size, which leads to an increased surface‐area‐to‐volume ratio of the particles. This interpretation is supported by a theoretical formalism developed based on substituent accumulation within the space‐charge layers, which predicts how the technical limit depends on the surface‐volume fraction. A Li// Li 6.4 P 0.6 Si 0.4 S 5 Br//Li symmetric cell demonstrates excellent Li plating and stripping over extended cycling. A full cell incorporating Li 6.4 P 0.6 Si 0.4 S 5 Br retains ≈67% (96 mAh g −1 ) of its initial capacity (143 mAh g −1 ) after 50 cycles at 0.2 C, and delivers 76 mAh g −1 at 1 C.