Structure Formation of Polycarbide-Based TiC-VC(NbC)-WC/nano WC Hard Alloys

The process of structure formation in the alloys of the system TiC-VC(NbC)-NiCr with the alloying additions of the fine or nano WC, depending on the chemical composition and sintering temperature using the optical microscopy, SEM and XRD analysis, is investigated in this paper. The core/rim structure alloys were found irrespective of the amount of tungsten carbide additions. The research suggests that the adding of nano WC causes decrease in carbide grains, redistribution of the elements in the core and rim, and decrease in sintering temperature by 50–100 °С. Tika pētīts struktūru veidosanas process sakausējumos TiC-VC(NbC)-NiCr ar smalku vai nano WC sakausējuma papildinājumiem atkarībā no ķīmiskā sastāva un saķepināsanas temperatūras, izmantojot optisko mikroskopiju, SEM un XRD analīzi. Centru/aptvērumu struktūras sakausējumi tika konstatēti neatkarīgi no volframa karbīda piedevu daudzuma. Pētījums liecina, ka nano WC pievienosana samazina karbīda graudus, elementu pārdali centros un aptvērumos, kā arī notiek saķepināsanās temperatūras samazināsanās par 50–100° С.