ELECTROCHEMICAL CORROSION REPORT FOR TANKS 241-AW-103 & 241-AZ-102 & 241-AN-106 & 241-AN-107 & 241-AY-101 & 241-AY-102

Corrosion rates using supernatant samples retrieved from near the top of the liquid layer were determined for the tanks. Corrosion rates using settled solids (saltcake) were determined. The supernatant samples were tested as received without argon sparging. The settled solid sample segments were extruded under anaerobic condition and kept under a sweep of humidified argon gas during 'the electrochemical corrosion testing. The class of steel used to construct the tank in question was used, and test coupons were allowed to equilibrate for a minimum of 18 hours before a Tafel scan was initiated. The coupons were scanned from -250 mV to +250 mV from the rest or open circuit potential. The corrosion rate is reported along with the corrosion current measurement, open circuit potential, and a chi-square statistic generated by the instrument controlling and analysis algorithm