Open AccessMechanistic dissimilarities between environmentally-influenced fatigue-crack propagation at near-threshold and higher growth rates in lower-strength steels
Author(s) -
S. Suresh,
Robert O. Ritchie
Publication year - 1981
Language(s) - English
Resource type - Reports
DOI - 10.2172/5532223
Subject(s) - crack closure , piping , corrosion fatigue , hydrogen embrittlement , hydrogen , materials science , fracture mechanics , fractography , stress corrosion cracking , paris' law , growth rate , cracking , corrosion , stress concentration , range (aeronautics) , embrittlement , metallurgy , composite material , chemistry , thermodynamics , physics , geometry , mathematics , organic chemistry