High temperature solder alloys for underhood applications: Final report
Author(s) -
Jeff Kern,
Celeste A. Drewien,
F.G. Yost,
S. Sackinger,
M. Weiser
Publication year - 1996
Language(s) - English
Resource type - Reports
DOI - 10.2172/258183
Subject(s) - intermetallic , soldering , eutectic system , materials science , isothermal process , metallurgy , ternary operation , microstructure , thermodynamics , alloy , physics , computer science , programming language
In this continued study, the microstructural evolution and peel strength as a function of thermal aging were evaluated for four Sn-Ag solders deposited on double layered Ag-Pt metallization. Additionally, activation energies for intermetallic growth over the temperature range of 134 to 190{degrees}C were obtained through thickness measurements of the Ag-Sn intermetallic that formed at the solder-metallization interface. It was found that Bi-containing solders yielded higher activation energies for the intermetallic growth, leading to thicker intermetallic layers at 175 and 190{degrees}C for times of 542 and 20.5 hrs, respectively, than the solders free of Bi. Complete reaction of the solder with the metallization occurred and lower peel strengths were measured on the Bi-containing solders. In all solder systems, a Ag-Sn intermetallic thickness of greater than {approximately}7 {mu}m contributed to lower peel strength values. The Ag-Sn binary eutectic composition and the Ag-Sn-Cu ternary eutectic composition solders yielded lower activation energies for intermetallic formation, less microstructural change with time, and higher peel strengths; these solder systems were resilient to the effects of temperatures up to 175{degrees}C. Accelerated isothermal aging studies provide useful criteria for recommendation of materials systems. The Sn-Ag and Sn-Ag-Cu eutectic compositions should be considered for future service life and reliability studies based upon their performance in this study

The content you want is available to Zendy users.

Already have an account? Click here to sign in.
Having issues? You can contact us here