Multi-Function Waste Tank Facility Corrosion Test Report (Phase 1)

This report documents the results of the corrosion tests that were performed to aid in the selection of the construction materials for multi-function waste tanks to be built in the U.S. Department of Energy Hanford Site. Two alloys were tested: 304L and Alloy 20 austenitic stainless steel. The test media were aqueous solutions formulated to represent the extreme of the chemical compositions of waste to be stored in the tanks. The results summerized by alloy are as follows: For 304L the tests showed no stress-corrosion cracking in any of the nine test solutions. The tests showed pitting in on of the solutions. There were no indications of any weld heat-tint corrosion, nor any sign of preferential corrosion in the welded areas. For Alloy 20 the tests showed no general, pitting, or stress-corrosion cracking. One crevice corrosion coupon cracked at the web between a hole and the edge of the coupon in one of the solutions. Mechanical tests showed some possible crack extension in the same solution. Because of the failure of both alloys to meet test acceptance criteria, the tank waste chemistry will have to be restricted or an alternative alloy tested