Observations of Fatigue Crack Initiation and Damage Growth in Notched Titanium Matrix Composites

The purpose was to characterize damage initiation and growth in notched titanium matrix composites at room temperature. Double edge notched or center open hole SCS-6/Ti-15-3 specimens containing 0 deg plies or containing both 0 and 90 deg plies were fatigued. The specimens were tested in the as-fabricated (ASF) and in heat-treated conditions. A local strain criterion using unnotched specimen fatigue data was successful in predicting fatigue damage initiation. The initiation stress level was accurately predicted for both a double edge notched unidirectional specimen and a cross-plied center hole specimen. The fatigue produced long multiple cracks growing from the notches. These fatigue cracks were only in the matrix material and did not break the fibers in their path. The combination of matrix cracking and fiber/matrix debonding appears to greatly reduce the stress concentration around the notches. The laminates that were heat treated showed a different crack growth pattern. In the ASF specimens, matrix cracks had a more tortuous path and showed considerable more crack branching. For the same specimen geometry and cyclic stress, the (0/90/0) laminate with a hole had far superior fatigue resistance than the matrix only specimen with a hole.