Degradation Analysis of Jute Fiber Reinforced Waste Tile Powder-Filled Polymer Composite on Wear Characteristics

In this study, a polymer composite is made using chemically treated jute fiber and waste floor tile powder as an alternative source for roof tile application. The wear qualities were examined at various ages, and the outcomes were optimized. In order to improve the wetting properties of the jute fiber, it was chemically treated. MINITAB software was used to develop Taguchi method parameters such as jute fiber percentage, waste tile powder percentage, and NaOH chemical treatment using the MINITAB software. It was determined that hardness was the most important characteristic in terms of wear properties after the specimens were subjected to ageing and abrasion wear testing and hardness tests were carried out as per normal protocols. As a result of the waste tile powder addition, the surface and core pore formation rates were reduced and the wear index rates were low. Jute fiber with 15%, 9% tile powder, and 5% NaOH treatment were found to have the lowest wear index of the other specimen compositions tested, according to the wear index. Specimen made with 5% jute fiber addition, 9% tile powder inclusion, and 10% NaOH treatment, on the other hand, had more hardness. Degradation of the fibers and delamination are side effects of the ageing process. The wear resistance of the surface was increased by the use of waste tile powder.