English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Plus monthly

Global: Zendy Tools annual

Global: Zendy Tools monthly

Global: Zendy Free Plan

Cables/hangers are important load-bearing components of suspension, cable-stayed, and through-arch bridges. Their reliability throughout their service life directly affects the safety of these bridges. In this study, to provide a reference for the design, maintenance, and inspection of bridge cables/hangers, their damage and failure mechanisms were theoretically analyzed using finite element analysis and corrosion-fatigue simulation tests of steel wires, based on the characteristics of the cable/hanger damage. The finite element analysis showed that a rotation of 0.00113 rad in the lower anchorage area results in a bending stress of 18.8 MPa, indicating that the effect of the bending stress on the steel wires in this area cannot be neglected, as it is a factor contributing to the failure of long cables/hangers. We further used a salt spray chamber to simulate an acid-rain environment. The results showed the following: (1) corrosion-fatigue damage of the cables/hangers occurs under the combined action of a corrosive environment and an alternating stress. This leads to an intensified corrosion damage, reduced ductility, increased brittleness, and eventually, brittle fracturing of the cables/hangers. (2) In the same corrosive environment, the highest degree of specimen corrosion occurred during alternating stress, followed by static stress, and no stress. (3) After corrosion-fatigue damage occurred for a specimen, its breaking stress was about 60% in comparison to the uncorroded specimen. The percentage elongation at the break also decreased; this was about 40% in comparison to the uncorroded specimen, indicating brittle fracturing. (4) The steel wires of the cables/hangers with corrosion-fatigue damage are more prone to brittle fracture if they are exposed to complex spatial stresses.

Analysis of Corrosion-Fatigue Damage and Fracture Mechanism of In-Service Bridge Cables/Hangers