Xe Ion Irradiation-Induced Microstructural Evolution and Hardening Effect of Nickel-Base Superalloy
Author(s) -
Yu Hou,
De-hui Li,
Yanling Lü,
Hefei Huang,
W. Z. Yang,
Ren-Duo Liu
Publication year - 2021
Publication title -
science and technology of nuclear installations
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.417
H-Index - 24
eISSN - 1687-6083
pISSN - 1687-6075
DOI - 10.1155/2021/5535478
Subject(s) - materials science , irradiation , nanoindentation , hardening (computing) , fluence , superalloy , transmission electron microscopy , ion , nanoindenter , metallurgy , microstructure , dislocation , composite material , nanotechnology , chemistry , physics , organic chemistry , layer (electronics) , nuclear physics
The nickel-base superalloy Hastelloy N was irradiated using 1 MeV Xe20+ and 7 MeV Xe26+ ions with displacement damage ranging from 0.5 dPa to 10 dPa at room temperature (RT). The irradiated Ni-based superalloy was characterized with transmission electron microscopy (TEM), XRD, and nanoindenter to determine the changes in microstructural evolution and nanoindentation hardness. The TEM results showed that ion irradiation induced a large number of defects such as black spots and corrugated structures and the second phase was rapidly amorphized after being irradiated to a fluence of 0.5 dPa. The XRD results showed that the Hastelloy N alloy sample did not undergo lattice distortion after ion irradiation. An obvious irradiation hardening phenomenon was observed in this study, and the hardness increased with Xe ion fluence. The pinning effect in which the defects can become obstacles to the free movement of dislocation may be responsible for the irradiation-induced hardening.

The content you want is available to Zendy users.

Already have an account? Click here to sign in.
Having issues? You can contact us here
Accelerating Research

Address

John Eccles House
Robert Robinson Avenue,
Oxford Science Park, Oxford
OX4 4GP, United Kingdom