Microstructural Investigations of Rapidly Solidified Al-Co-Y Alloys
Author(s) -
Barış Avar,
Musa Göğebakan,
Mehmet Tarakçı,
Yücel Gençer,
Süleyman Kerli̇
Publication year - 2013
Publication title -
advances in materials science and engineering
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.356
H-Index - 42
eISSN - 1687-8442
pISSN - 1687-8434
DOI - 10.1155/2013/163537
Subject(s) - materials science , differential scanning calorimetry , supercooling , amorphous solid , alloy , microstructure , analytical chemistry (journal) , crystallography , metallurgy , thermodynamics , chemistry , physics , chromatography
The alloys with different compositions in the Al-rich corner of the Al-Co-Y ternary system were prepared by conventional casting and further processed by melt-spinning technique. The microstructure and the thermal behavior of the alloys were analyzed by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and differential thermal analysis (DTA). It was found that only rapidly solidified Al85Co7Y8 alloy exhibited the best glass forming ability (GFA) and a fully amorphous structure. Besides, Al85Co13Y2 and Al85Co2Y13 alloy ribbons were fully crystalline, whereas Al85Co10Y5 and Al85Co5Y10 alloy ribbons consisted of some crystalline phases within an amorphous matrix. The SEM results showed the same trend that the crystalline phase fraction decreases with the approaching into best glass former. From DSC results, only Al85Co7Y8 amorphous alloy exhibited a glass transition temperature (Tg) at 569 K, and its supercooled liquid region (ΔTx=Tx−Tg) was found to be 17 K. Moreover, other calculated GFA parameters for this alloy system were also discussed

The content you want is available to Zendy users.

Already have an account? Click here to sign in.
Having issues? You can contact us here
Accelerating Research

Address

John Eccles House
Robert Robinson Avenue,
Oxford Science Park, Oxford
OX4 4GP, United Kingdom