Open AccessStudy on a new composite gel system
Author(s) -
Yi Sun,
Gao Wei,
Ding-Xue Zhang
Publication year - 2021
Publication title -
journal of physics. conference series
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.21
H-Index - 85
eISSN - 1742-6596
pISSN - 1742-6588
DOI - 10.1088/1742-6596/2009/1/012072
Subject(s) - composite number , viscometer , viscosity , silica gel , materials science , composite material , polyacrylamide , rheology , chromatography , chemistry , polymer chemistry
A composite gel system was developed to solve the problems of low gel forming viscosity, gel forming and high salinity resistance in pH range of 6~8. The viscosity of the gel was determined by rotary viscometer, and the performance of the composite gel was analyzed. The pH of the composite gel, the gelation property of the mineralized degree and the plugging test of the sand filling pipe and the oil displacement experiment were carried out. The results showed that the gel performance of the composite gel was better than that of the conventional gel system at 60 degrees Celsius. The viscosity of the composite gel reached 10000 mPa S, at 0.1% polyacrylamide concentration, the gel forming range of pH was 6~12, and the viscosity of 20000 mg/L NaCl solution reached 15000 mPa/s, which had better salt resistance. The plugging test of sand filling pipe showed that the plugging rate of the gel to permeation layer was close to 90%, and the plugging ability was better. After 18% 0.2pv injection, the recovery rate increased by about 18%, which can meet the requirements of profile control in most oilfields.