Effect of surface passivation process for AlGaN/GaN HEMT heterostructures using phenol functionalized-porphyrin based organic molecules

In this work, we investigate an unexplored possibility of passivating the charged surface states on AlGaN/GaN high electron mobility transistor (HEMT) heterostructures by using organic molecules. This has further led to remarkable enhancement in the electrical properties of rectifying metal-semiconductor contacts on AlGaN/GaN. Phenol functionalized Zinc metallated-Tetra Phenyl Porphyrin (Zn-TPPOH) organic molecules were adsorbed on AlGaN/GaN via the solution phase to form a molecular layer (MoL). The presence of the MoL was confirmed using X-ray Photoelectron Spectroscopy (XPS). The thickness of the MoL was assessed as ∼1 nm, using Spectroscopic Ellipsometry and cross-sectional Transmission Electron Microscopy. XPS peak-shift analyses together with Kelvin Probe Force Microscopy revealed that the molecular surface modification reduced the surface potential of AlGaN by approximately 250 meV. Consequently, the Barrier height (ideality factor) of Ni Schottky diodes on AlGaN/GaN was increased (reduced) significantly from 0.91 ± 0.05 eV (2.5 ± 0.31) for Ni/AlGaN/GaN to 1.37 ± 0.03 eV (1.4 ± 0.29) for Ni/Zn-TPPOH/AlGaN/GaN. In addition, a noteworthy decrement in the reverse current from 2.6 ± 1.93 μA to 0.31 ± 0.19 nA at −5 V (∼10 000 times) was observed from Current-Voltage (I-V) measurements. This surface-modification process can be fruitful for improving the performance of AlGaN/GaN HEMTs, mitigating the adverse effects of surface states and polarization in these materials.In this work, we investigate an unexplored possibility of passivating the charged surface states on AlGaN/GaN high electron mobility transistor (HEMT) heterostructures by using organic molecules. This has further led to remarkable enhancement in the electrical properties of rectifying metal-semiconductor contacts on AlGaN/GaN. Phenol functionalized Zinc metallated-Tetra Phenyl Porphyrin (Zn-TPPOH) organic molecules were adsorbed on AlGaN/GaN via the solution phase to form a molecular layer (MoL). The presence of the MoL was confirmed using X-ray Photoelectron Spectroscopy (XPS). The thickness of the MoL was assessed as ∼1 nm, using Spectroscopic Ellipsometry and cross-sectional Transmission Electron Microscopy. XPS peak-shift analyses together with Kelvin Probe Force Microscopy revealed that the molecular surface modification reduced the surface potential of AlGaN by approximately 250 meV. Consequently, the Barrier height (ideality factor) of Ni Schottky diodes on AlGaN/GaN was increased (reduced) signifi...