Super‐Ionic Conductivity in ω‐ Li 9 Tr P 4 ( Tr = Al, Ga, In) and Lithium Diffusion Pathways in Li 9 AlP 4 Polymorphs
Author(s) -
Restle Tassilo M. F.,
Strangmüller Stefan,
Baran Volodymyr,
Senyshyn Anatoliy,
Kirchhain Holger,
Klein Wilhelm,
Merk Samuel,
Müller David,
Kutsch Tobias,
Wüllen Leo,
Fässler Thomas F.
Publication year - 2022
Publication title -
advanced functional materials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 6.069
H-Index - 322
eISSN - 1616-3028
pISSN - 1616-301X
DOI - 10.1002/adfm.202112377
Subject(s) - materials science , ionic conductivity , neutron diffraction , conductivity , octahedron , lithium (medication) , fast ion conductor , crystallography , ion , activation energy , analytical chemistry (journal) , crystal structure , chemistry , electrolyte , medicine , organic chemistry , electrode , endocrinology , chromatography
Phosphide‐based compounds are promising materials for solid electrolytes. In recent times, a multiplicity of compounds featuring isolated M P 4 ( M = Si,Ge,Sn,Al,Ga) tetrahedra as structural building units in different arrangements with superionic lithium conductivity have been discovered. ω‐Li 9 AlP 4 , ω‐ Li 9 GaP 4 , and ω‐Li 9 InP 4 are presented as new high‐temperature modifications with superionic lithium conductivity reaching 4.5 mS cm −1 at room temperature. Impedance spectroscopy and static temperature‐dependent 7 Li NMR experiments reveal conductivity values in the range of 0.2 to 4.5 mS cm −1 at room temperature and low activation energies for the title compounds. X‐ray and neutron diffraction methods disclose that the phosphorus atoms form a cubic‐close packing. The triel element and Li atoms are located in tetrahedral voids, further Li atoms partially fill the octahedral voids. Temperature‐dependent neutron diffraction shows for Li 9 AlP 4 a phase transition at 573 K that influences the occupation of voids with Li and significantly affects the Li‐ion mobility. The evaluation of nuclear scattering densities by the maximum‐entropy approach and application of the one‐particle‐potential formalism reveal 3D lithium diffusion with a low activation energy preferentially on paths of adjacent tetrahedral and octahedral voids. The investigation of different polymorphs suggests that the equilibrated filling of tetrahedral and octahedral voids is a crucial parameter for the enhancement of superionic lithium conductivity.