English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

This paper presents the results obtained from the chemical activation of bacterial nanocellulose (BCN) using fique juice as a culture medium. BNC activation (BNCA) was carried out with H 3 PO 4 and KOH at activation temperatures between 500 °C to 800 °C. The materials obtained were characterized morphologically, physicochemically, superficially, and electrochemically, using scanning electron microscopy, X-ray photoelectron spectroscopy (XPS), the physisorption of gases N 2 and CO 2 at 77 K and 273 K, respectively, cyclic voltammetry, chronopotentiometry, and electrochemical impedance spectroscopy (EIS). The samples activated with H 3 PO 4 presented specific surface areas (S BET ) around 780 m 2 g -1 , while those activated with KOH values presented specific surface areas between 680 and 893 m 2 g -1 . The XPS analysis showed that the P XPS percentage on the surface after H 3 PO 4 activation was 11 wt%. The energy storage capacitance values ranged between 97.5 F g -1 and 220 F g -1 by EIS in 1 M H 2 SO 4 . The samples with the best electrochemical performance were activated with KOH at 700 °C and 800 °C, mainly due to the high S BET available and the accessibility of the microporosity. The capacitance of BNCAs was mainly improved by electrostatic effects due to the S BET rather than that of pseudocapacitive ones due to the presence of phosphorus heteroatoms.

polymers

Bacterial Nanocellulose from Komagataeibacter Medellinensis in Fique Juice for Activated Carbons Production and Its Application for Supercapacitor Electrodes