English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Zendy Plus

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Zendy Tools

Zendy Open

In this study, the effects of the post-ultraviolet-curing process on the flexural, absorptive, and morphological properties of poly(lactic acid) specimens produced using a fused deposition modelling technique 3D printer were experimentally investigated. In this direction, 15, 30, 45, and 60 min post-UV-curing processes were applied to poly(lactic acid) three-point bending and absorption specimens produced at 190 and 200 °C. Three-point bending tests and morphological analyses were applied after the post-ultraviolet-curing process, and absorption tests were applied by immersing the post-ultraviolet-cured specimens in a distilled water bath for 1-, 3-day, and 1-, 2-, and 4-week exposure times. The changes in flexural strain properties for each experimental parameter were also simulated by the computer-aided finite element analysis and compared with the experimental results. It was observed that the post-ultraviolet-curing process increased the flexural strength of the poly(lactic acid) specimens produced at both 190 and 200 °C with the same increasing trend up to 30 min of exposure, and the most significant increase was determined in the specimens that were subjected to post-ultraviolet-curing for 30 min. Although the flexural strengths of the post-ultraviolet-cured specimens were higher than the non-cured specimens in all conditions, it was detected that they tended to decrease after 30 min.

Effects of Post-UV-Curing on the Flexural and Absorptive Behaviour of FDM-3D-Printed Poly(lactic acid) Parts