English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Τhis work describes the synthesis of PLA-grafted M-alginate (g-M-alginate; M: Ca2+, Co2+, Ni2+, Cu2+) aerogels. DL-lactide (LA) was attached on the surface of preformed M-alginate beads and was polymerized, using stannous octoate as catalyst and the –OH groups of the alginate backbone as initiators/points of attachment. The material properties of g-M-alginate aerogels were not affected much by grafting, because the linear PLA chains grew on the M-alginate framework like a brush and did not bridge their points of attachment as in polyurea-crosslinked M-alginate aerogels. Thus, all g-M-alginate aerogels retained the fibrous morphology of their parent M-alginate aerogels, and they were lightweight (bulk densities up to 0.24 g cm−3), macroporous/mesoporous materials with high porosities (up to 96% v/v). The BET surface areas were in the range of 154–542 m2 g−1, depending on the metal, the nature of the alginate framework and the PLA content. The latter was found at about 15% w/w for Ca- and Ni-based materials and at about 29% w/w for Co- and Cu-based materials. Overall, we have demonstrated a new methodology for the functionalization of alginate aerogels that opens the way to the synthesis of polylactide-crosslinked alginate aerogels with the use of multifunctional monomers.

Polylactide-Grafted Metal-Alginate Aerogels