Preferential Grain Orientation in Hot Pressed TiB 2

Author(s) -

Jensen Morten Sundheim,

Einarsrud MariAnn,

Grande Tor

Publication year - 2007

Publication title -

journal of the american ceramic society

Language(s) - English

Resource type - Journals

SCImago Journal Rank - 0.9

H-Index - 196

eISSN - 1551-2916

pISSN - 0002-7820

DOI - 10.1111/j.1551-2916.2007.01623.x

Subject(s) - materials science , titanium diboride , anisotropy , diffraction , titanium , orientation (vector space) , titanio , metallurgy , metallography , composite material , x ray crystallography , crystallography , microstructure , optics , chemistry , geometry , transition metal , ceramic , biochemistry , physics , mathematics , catalysis

Preferential grain growth is reported for hot pressed titanium diboride (TiB 2 ) prepared at 1800°C and 50 MPa. Orientation imaging microscopy and X‐ray diffraction revealed that the grains in the material were preferentially orientated with the [001] direction parallel to the mechanical field. The experimental findings are discussed, with emphasis on the anisotropic properties of TiB 2 .