English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

A fully computerized system of spray pyrolysis was employed for fabricating copper tin sulphite ternary thin film onto glass substrates. During deposition process, the glass substrate was maintained at 310 ± 10 °C. After dissolving the raw chemicals, a mixture of their aqueous solutions was used for spraying process. The optimum solution mixture at the volumetric ratio [S/(Cu+Sn)=1] at 1.5 of pH. XRD investigation was approved a monoclinic phase of CTS. A number of different platform speed was tested in the deposition process. XRD diffraction peaks were described at 2θ = 28.39°, 33.02°, 47.34°, and 56.39° corresponding to the    ( 2 ¯ 1 ¯ 1 ) ( 2 ¯ 0 6 ) , ( 2 ¯ 0 10 ) , and    ( 3 ¯ 2 ¯ 10 ) , respectively. These are crystal planes of monoclinic copper tin sulphide. The FTIR study certified a number of the chemical bond of Cu-, Sn- and S-. The grain size was observed in the range of nano using Scherrer formula. Studying surface morphology of CTS films reveals a uniform coating on the substrates which approved by SEM investigations.

Ternary Cu2SnS3 Thin Films Deposited by Fully Controlled System of Spray Pyrolysis