New Compounds in the IMb 2 O 6 (Ta 2 O 5 )‐V 2 O 6 Systems

In the Nb 2 O 5 –V 2 O 5 and Ta 2 O 5 –V 2 O 5 systems, new compounds, 9Nb 2 O 5 · 2V 2 O 5 and 9Ta 2 O 5 · 2V 2 O 5 , are formed at low temperatures from amorphous materials prepared by the simultaneous hydrolysis of either niobium isopropoxide or tantalum isopropoxide and vanadyl ethoxide. They are isomorphous and have an orthorhombic unit cell, with a = 0.7939 nm, b = 1.731 nm, and c = 1.761 nm for the former compound and a = 0.7859 nm, b = 1.733 nm, and c = 1.766 nm for the latter compound. Both compounds decompose into 9Nb 2 O 5 · V 2 O 5 (9Ta 2 O 5 · V 2 O 5 ) and V 2 O 5 at elevated temperatures. Neue Verbindungen in Nb 2 O 5 (Ta 2 O 5 ) –V 2 O 5 ‐Systemen Inhaltsübersicht. In den Nb 2 O 5 –V 2 O 5 ‐ und Ta 2 O 5 –V 2 O 5 ‐Systemen werden die neuen Verbindungen 9Nb 2 O 5 · 2V 2 O 5 und 9Ta 2 O 5 · 2V 2 O 5 bei niedrigen Temperaturen aus amorphen, durch simultane Hydrolyse von Niobisopropoxid bzw. Tantalisopropoxid und Vanadylethoxid erhaltenen Substanzen gebildet. Sie sind isomorph und haben eine orthorhombische Einheitszelle mit a = 0,7939, b = 1,731, c = 1,761 nm für erstere und a = 0,7859, b = 1,733, c = 1,766 nm für letztere Verbindung. Beide Verbindungen zerfallen bei erhöhter Temperatur in 9Nb 2 O 5 · V 2 O 5 bzw. 9Ta 2 O 5 . V 2 O 5 und V 2 O 5 .