Bimetallic Au–Pd Nanoparticles Confined in Tubular Mesoporous Carbon as Highly Selective and Reusable Benzyl Alcohol Oxidation Catalysts
Author(s) -
Hao Yan,
Hao GuangPing,
Guo DeCai,
Guo ChunZao,
Li WenCui,
Li MingRun,
Lu AnHui
Publication year - 2012
Publication title -
chemcatchem
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 1.497
H-Index - 106
eISSN - 1867-3899
pISSN - 1867-3880
DOI - 10.1002/cctc.201200207
Subject(s) - benzyl alcohol , bimetallic strip , high resolution transmission electron microscopy , catalysis , mesoporous material , nanoparticle , incipient wetness impregnation , materials science , furfuryl alcohol , chemical engineering , selectivity , transmission electron microscopy , chemistry , nanotechnology , organic chemistry , engineering
Abstract Size‐uniform and highly dispersed bimetallic Au–Pd nanoparticles were formed in situ and confined in tubular mesoporous carbon by successive incipient wetness impregnation and a thermal annealing method. The bimodal mesoporous carbon (CMK‐5) encapsulated Au–Pd nanoparticles with 1 wt % metal loading enables superior activity compared with mono‐modal mesoporous carbon for benzyl alcohol oxidation. A conversion of >99 % and selectivity of >99 % can be reached within 3 h under mild conditions, for example, at 80 °C and at atmospheric pressure. It is found that during the catalyst preparation, the Au and Pd precursor impregnation sequence is a key factor to the formation of Au–Pd nanoparticles under identical conditions. A relatively high activity is realized by the first impregnation of the Au precursor, followed by the second impregnation of the Pd precursor. The crystalline structure and distribution of Au–Pd nanoparticles are characterized by high‐resolution transmission electron microscopy (HRTEM), energy‐dispersive X‐ray spectroscopy (EDX), and XRD. It is found that a larger proportion of surface‐exposed Pd atoms in Au–Pd nanoparticles have a positive effect on catalytic activity. The Au–Pd nanoparticles have a narrow size distribution that is concentrated at approximately 4 nm. TEM and N 2 adsorption results reveal that the catalyst has a large surface area and well‐developed bimodal pore interconnectivity, which contribute to its excellent activity. The used catalyst retained a high selectivity but conversion decreased with recycling. The deactivation mechanism was attributed to the tiny amount of incompletely removed benzaldehyde adsorbed onto the active surface, which blocked access from the active sites to benzyl alcohol. Importantly, the used catalyst can be recovered by a simple heat treatment at 200 °C in air after the catalytic cycles have completed; the adsorbed benzaldehyde is removed from the active surface. Hence, Au–Pd nanoparticles confined in tubular mesoporous carbon can be used as an alternative method to develop highly dispersed nanocatalysts to improve catalytic efficiency.