English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

The corrosion behavior of high strength low alloy AISI 4135 steel was studied following extended exposure to a Qingdao field environment. When electrochemically active γ-FeOOH was formed in conjunction with easily reducible β-FeOOH, these corrosion products acted to accelerate corrosion attack in the marine splash zone (i.e., steel structure above the water line that is splashed by sea spray). It had also been observed that the pH beneath the rust layer exhibited a minimum during the non-splash part of wet and non-splash corrosion cycling. These acidic conditions contributed significantly to an increase in the rate of localized corrosion, both beneath the rust deposits and within rust cracks and voids within pockets of rust deposits over the steel surface

Corrosion Performance of High Strength Low Alloy Steel AISI 4135 in the Marine Splash Zone