English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

The glass formation and the dissolution property in -FeO-CuO system were studied. In the batch process, the content of P2O5 was fixed at 60mol% and the other elements were varied from 10~40mol%. The prepared glasses were soaked in the D.I. water up to 13hr and the dissolution properties were investigated with the solutions sampled every 2 hr. The result shows that the was leached out firstly from Phosphate glass system and then Cu and Fe ions were observed according to atmosphere change in solution. ICP shows that the dissolution amount in Phosphate was depended on the glass structure and the highest dissolution amount of CuO and FeO ions was observed when the 10mol% was added in batch process.

Glass Formation and Ion Dissolution of P2O5-K2O-FeO-CuO Glasses

Glass Formation and Ion Dissolution of P₂O₅-K₂O-FeO-CuO Glasses