English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Bu çalışma, yüksek hızlı oksi yakıt (HVOF) ısıl püskürtme yöntemi ile SAE 4140 çeliği üzerinde üretilen WCCo-Mo kompozit kaplamaların mikroyapısal özelliklerini araştırmak için yapılmıştır. Bu amaç için WCCo tozlarına ilave edilen Mo miktarı % ağ. 10, 20, 30 ve 40 olarak değiştirilmiştir. Kaplamalar, faz bileşimi, mikroyapı ve sertlik özellikleri açısından karşılaştırılmıştır. Kaplama tabakalarının faz bileşimi ve mikroyapısı X-ışını difraktogramı (XRD) ve taramalı elektron mikroskobu (SEM) ile incelenmiştir. XRD sonuçları, WCCo-Mo kaplama tabakasının WC, W2C, Co3W3C, Mo2C, MoO2, Mo ve Co fazlardan oluştuğunu göstermiştir. Kaplamaların sertliği Mo artışı ile artmıştır.The present study has been carried out in order to investigate the microstructural properties of WCCo-Mo composite coatings deposited onto a SAE 4140 steel substrate by high velocity oxygen fuel (HVOF) thermal spray. For this purpose, the Mo quantity added to the WCCo was changed as 10, 20, 30 and 40 wt. % percents. The coatings are compared in terms of their phase composition, microstructure and hardness. Phase compound and microstructure of coating layers were examined using X-ray diffractometer (XRD) and scanning electron microscope (SEM). XRD results showed that WCCo-Mo composite coatings were mainly composed of WC, W2C, Co3W3C, Mo2C, MoO2, Mo and Co phases. The average hardness of the coatings increased with increasing Mo content

Microstructure Characterization of WCCo-Mo Based Coatings Produced Using High Velocity Oxygen Fuel