English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Plus monthly

Global: Zendy Tools annual

Global: Zendy Tools monthly

Global: Zendy Free Plan

The objective of this study is to investigate the brazeability of a new laminated composite with Ni-Cr-P filler metal in vacuum. Microstructure, microhardness and shear strength of the brazed joint were investigated by means of scanning electron microscopy, energy-dispersive spectroscopy, microsclerometer and electromechanical universal testing machine. Excellent joint of super-Ni/NiCr laminated composite to Cr18-Ni8 steel was obtained at 1040◦C for 20 min through vacuum brazing with Ni-Cr-P filler metal. Ni2Cr particles precipitated in NiCr base layer under the influence of thermal cycle. The brazed region consisted of γ-Ni(Cr) solid solution and eutectic of γ-Ni(P) and Ni3P. Microhardness of the eutectic was as high as 630 HV. Shear strength of the brazed joint was 137 MPa and the joint fractured in the eutectic. Steps and cracks formed in the fracture surface under the shear force. K e y w o r d s: laminate, super-Ni/NiCr, vacuum brazing, Ni-Cr-P, microstructure

Microstructure and fracture characteristics in vacuum brazed joint of super-Ni/NiCr laminated composite