English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Formation of microstructure defects at the phase boundaries in TRIP steels was investigated with the aid of microstructure analysis on a TRIP steel crystal, which was grown by the Bridgman technique. The microstructure studies comprised scanning electron microscopy (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD), transmission electron microscopy (TEM) and transmission electron microscopy with high resolution (HRTEM). Initial XRD measurements revealed that the crystals under study consist of austenite and ferrite with extremely strong preferred orientations. Subsequent XRD pole figure measurements and EBSD scans have shown that the orientation relationship between austenite and ferrite can be described by the Nishiyama-Wassermann model. For a detailed description of the microstructure of the Bridgman crystal, the orientation distribution of crystallites within the individual phases was investigated using the XRD reciprocal space mapping and the rocking curve measurements. These experiments have shown that the density of microstructure defects is much lower in ferrite than in austenite. The direct information about the defect structures at the phase boundaries between austenite and ferrite was obtained from the TEM micrographs, which revealed complicated micro-twin structures at the boundaries between the neighbouring phases. HRTEM discovered very narrow stripes of ferrite embedded in austenite that were regarded as a source of the microstructure defects in austenite.

Microstructure Investigations of the Phase Boundaries in the Bridgman TRIP Steel Crystal