English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

This work applies a combination of immersion tests, surface analysis techniques, and electrochem­ical methods to characterise the degradation process of AZ31 magnesium alloy when it is exposed to artificial saliva for 28 days. The surface of the alloy was evaluated in two conditions: bare and with an MgF2 layer. This conversion layer was formed by soaking AZ31 in hydrofluoric acid (HF). SEM images revealed differences in the corrosion attack of the two surface conditions, specifically in the vicinity of Al-Mn intermetallic particles. Both EDS and XPS analysis indicated that the composition of the corrosion layers formed during immersion tests corresponds mainly to Mg(OH)2 and Ca10(PO4)6(OH)2 for the bare sample, whereas for the treated surface the principal corrosion product was MgCO3. The polarisation resistance (Rp) value estimated from EIS experi­ments was two orders of magnitude higher for the HF-treated samples than that of the bare samples. In addi­tion, the corrosion rate (CR) calculated from the potentiodynamic polarisation (PDP) curves was lower for the HF-treated surface than for that of the bare AZ31 surface. All results indicate that the HF-treatment on AZ31 magnesium alloy surface improves significantly its corrosion resistance in artificial saliva.

Análisis del proceso de degradación y comportamiento electroquímico de la aleación de magnesio AZ31 en saliva artificial