English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Tools annual

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Presents the access of premium content as premium feature

Premium Content

Global: Zendy Plus annual

Global: Zendy Free Plan

Pure, highly chlorinated polyvinyl chloride (CPVC), with a 63 wt % of chlorine, showed a unique-thermal-pyrolytic-phenomenon that meant it could be converted to carbon material through solid-phase carbonisation rather than liquid-phase carbonisation. The CPVC began to decompose at 270 °C, with a rapid loss in mass due to dehydrochlorination and novel aromatisation and polycondensation up to 400 °C. In this study, we attempted to prepare carbon fibre (CF) without oxidative stabilisation, using the aforementioned CPVC as a novel precursor. Through the processes of solution spinning and solid-state carbonisation, the spun CPVC fibre was directly converted to CF, with a carbonisation yield of 26.2 wt %. The CPVC-derived CF exhibited a relatively smooth surface; however, it still demonstrated a low mechanical performance. This was because the spun fibre was not stretched during the heat treatment. Tensile strength, Young's modulus and elongation values of 590 ± 84 MPa, 50 ± 8 GPa, and 1.2 ± 0.2%, respectively, were obtained from the CPVC spun fibre, with an average diameter of 19.4 μm, following carbonisation at 1600 °C for 5 min.

Highly Chlorinated Polyvinyl Chloride as a Novel Precursor for Fibrous Carbon Material