English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Plus monthly

Global: Zendy Tools annual

Global: Zendy Tools monthly

Global: Zendy Free Plan

Gravitational melt-stir casting produced hybrid nano-reinforcements (β-SiCp) and micro-reinforcements (Bi and Sb) of AZ91 composites. SiCp-diffused discontinuous β-Mg17Al12 precipitation with a vital factor of SiC was exhibited at the grain boundary region, formulated Mg3Si throughout the composite and changed the present Mg0.97Zn0.03 phases. The creation of Mg2Si (cubic) and SiC (rhombohedral axes) enhanced the microhardness by 18.60% in a 0.5 wt.% SiCp/AZ91 matrix. The microhardness of 1 wt.% SiCp/AZ91 was slightly reduced after Mg0.97Zn0.03 (hexagonal) reduction. The best ultimate tensile value obtained was about 169.33 MPa (increased by 40.10%) in a 0.5 wt.% SiCp/AZ91 matrix. Microelements Bi and Sb developed Mg3Bi2, Mg3Sb2 and monoclinic C60 phases. The best peak yield strength of 82.75 MPa (increased by 19.85%) was obtained with the addition of 0.5 wt.% SiCp/1 wt.% Bi/0.4 wt.% Sb. The mismatch of the coefficient of thermal expansion of segregated particles and the AZ91 matrix, the shear transfer effect and the Orowan effect, combined with the quantitative value of phase existence, improved the compressive strengths of the composites with 0.5 wt.% β-SiCp, 1 wt.% β-SiCp and 0.5 wt.% SiCp/1 wt.% Bi/0.4 wt.% Sb by 2.68%, 6.23% and 8.38%, respectively. Notably, the Charpy impact strengths of 0.5 wt.% and 1 wt.% β-SiCp-added AZ91 composites were enhanced by 236% (2.89 J) and 192% (2.35 J), respectively. The addition of Bi and Sb with SiCp resulted in the formation of a massive phase of brittle Al6Mn. Al–Mn-based phases (developed huge voids and cavities) remarkably reduced impact values by 80% (0.98 J). The discussion covers the quantitative analyses of X-ray diffraction, optical microscopy and scanning electron microscopy results and fracture surfaces.

metals

Microstructure Evaluation, Quantitative Phase Analysis, Strengthening Mechanism and Influence of Hybrid Reinforcements (β-SiCp, Bi and Sb) on the Collective Mechanical Properties of the AZ91 Magnesium Matrix