English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Plus monthly

Global: Zendy Tools annual

Global: Zendy Tools monthly

Global: Zendy Free Plan

In this paper, the microstructure, defects, hardness, and tensile strength of the 17-4PH specimens manufactured additively using the selective laser melting (SLM) technique were studied. The analyzed parts (10 mm size cubic specimens and tensile specimens) were manufactured with different defocus parameter values (−1, 0, +1 mm) in order to evaluate this effect with a low power laser (38 W). The study was carried out on three different sections of each cubic specimen, one perpendicular to the laser beam or SLM manufacturing direction (transversal section), and another two parallel to the laser beam direction (longitudinal sections). The specimens microstructures were analyzed with an X-ray diffraction technique, as well as optical, scanning electron, and transmission electron microscopes. Image J software was used to characterize the defects and phase ratio. In addition, hardness and tensile tests were performed according to the corresponding standards. The results show that the amount of austenitic phase and the average grain size varied with defocusing. The percentage of defective area was less than 0.25%. The analyzed defocus distance did not affect the number and average size of the defects. Adjusting the defocusing SLM parameter is important for manufacturing parts with good mechanical properties.

Laser Defocusing Effect on the Microstructure and Defects of 17-4PH Parts Additively Manufactured by SLM at a Low Energy Input