English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Tools annual

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Presents the access of premium content as premium feature

Premium Content

Global: Zendy Plus annual

Global: Zendy Free Plan

In this study, the effects of Cr3C2, VC, and TaC on microstructure, WC grain morphology and mechanical properties of WC–10 wt. % Co ultrafine cemented carbides were investigated. The experimental results showed that WC grains size decreased and size distribution became narrow by adding Cr3C2, VC, and TaC. The inhibition efficiency was in the order of VC &gt; Cr3C2 &gt; TaC. Cr3C2 addition would induce triangular prism grains and Co phase was strengthened by Cr3C2, resulting in the enhancement of transverse rupture strength (TRS) and impact toughness. WC morphologies in cemented carbides with VC addition were triangular prisms with multi-steps in basal and prismatic planes due to anisotropic growth. The multi-steps in basal and prismatic planes led to low TRS and fracture toughness. The inhibition mechanism of TaC is to reduce the surface energy of WC and slow down the solution/re-precipitation rate at the WC/Co interfaces by adsorbing on the surface of WC grains. The sample with 0.8 wt. % Cr3C2 had excellent comprehensive mechanical properties. Its Vickers hardness, fracture toughness, TRS and impact toughness were 1620 kg/mm2, 9.94 MPa·m1/2, 3960 MPa and 50.4 J/m2, respectively. In summary, Cr3C2 is the first choice as the grain growth inhibitors (GGI) for the preparation of ultrafine cemented carbides.

Effects of Cr3C2, VC, and TaC on Microstructure, WC Morphology and Mechanical Properties of Ultrafine WC–10 wt. % Co Cemented Carbides