English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Tools annual

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Presents the access of premium content as premium feature

Premium Content

Global: Zendy Plus annual

Global: Zendy Free Plan

Recent studies have shown that the introduction of silicon can effectively improve the dielectric properties of polyimide (PI), and the introduction of a silicon–oxygen bond can increase the flexibility of the PI molecular structure, which is conducive to reducing the moisture absorption rate of PI materials. In this experiment, 1,3-bis(3-aminopropyl)-1,1,3,3-tetramethyl disiloxane (DSX) was mixed with 4,4′-diaminodiphenyl ether (ODA) in different proportions. A series of PI films containing silicon was obtained by random polymerization with pyromellitic dianhydride (PMDA), 3,3′,4,4′-diphenylketotetrahedral anhydride (BTDA) and biphenyl dianhydride (BPDA), and then tetrad copolymerization with three kinds of dianhydrides. At the same time, the PI structures were put into calculation software to obtain the simulated polarization results, and then the films were characterized by various properties. The results showed that the characterization results were consistent with that of simulation, and the best overall PI formula was when the ratio of diamines was 1:9 and mixed with PMDA. The performance data were as follows: the vitrification temperature was about 320 °C, T5 was 551 °C, water absorption was 1.56%, dielectric constant (Dk) was 2.35, dielectric loss (Df) was 0.007, tensile strength was 70 MPa and elongation at break was 10.2%.

Synthesis and Properties Comparison of Low Dielectric Silicon Containing Polyimides