English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Plus monthly

Global: Zendy Tools annual

Global: Zendy Tools monthly

Global: Zendy Free Plan

The influences of non-isothermal aging (the temperature range is 150-180 °C, and the heating rate is 5 and 20 °C/h alternately), single-peak aging (aging at 120 °C for 24 h, then water quenched was followed at room temperature), and two-stage aging (aging at 105 °C for 8 h first, then increasing aging temperature to 135 °C and keeping for 12 h, followed by water quenching at room temperature) on the corrosion resistance and microstructure of the 7N01 aluminum alloy under 3.5 wt.% NaCl were investigated using electric polarization curve test and exfoliation corrosion. After aging, the hardness of samples was measured by a Vickers micro-hardness tester, and the electrical conductivities were obtained using the eddy current method. The results show that the steady phase η and metastable phase η' are precipitated in the grain boundary of 7N01 aluminum alloy after non-isothermal aging, and their distribution is discontinuous. The hardness of the alloy can reach 136.9 HV1 and the electrical conductivity can reach 35.8% IACS, which is close to the hardness of single-peak aging and the conductivity of two-stage aging, respectively. Compared with single-peak aging, the corrosion current density of non-isothermal aging is reduced by 15.5%, and that of two-stage aging is reduced by 28.9%.

Effect of Aging Treatment on the Corrosion Resistance Properties of 7N01 Extrusion Aluminum Alloy