English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Nanocrystalline Eu(3+), Tb(3+) co-doped Lu(2)O(3) powders with a maximum size of 25.5 nm were prepared by the sol-gel process, using lutetium, europium and terbium nitrates as precursors, and ethanol as a solvent. Differential thermal analysis (DTA) and infrared spectroscopy (IR) were used to study the chemical changes during the xerogel annealing. After the sol evaporation at 100 °C, the formed gel was annealed from 300 to 900 °C for 30 min under a rich O(2) atmosphere, and the yielded product was analyzed by X-ray diffraction (XRD) to characterize the microstructural behavior and confirm the crystalline structure. The results showed that Lu(2)O(3) nanopowders start to crystallize at 400 °C and that the crystallite size increases along with the annealing temperature. A transmission electron microscopy (TEM) study of samples annealed at 700 and 900 °C was carried out in order to analyze the microstructure, as well as the size, of crystallites. Finally, in regard to scintillating properties, Eu(3+) dopant (5 mol%), Tb(3+) codoped Lu(2)O(3) exhibited a typical red emission at 611 nm (D(°)→(7)F(2)), furthermore, the effect of Tb(3+) molar content (0.01, 0.015 and 0.02% mol) on the Eu(3+) radioluminiscence was analyzed and it was found that the higher emission intensity corresponds to the lower Tb(3+) content.

Preparation and Scintillating Properties of Sol-Gel Eu3+, Tb3+ Co-Doped Lu2O3 Nanopowders