English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Tools annual

Global: Zendy Free Plan

Global: Zendy Tools monthly

Global: Zendy Plus monthly

Kesterite-structured Cu2ZnSnSe4 (CZTSe) is considered as one of the Earth-abundant and non-toxic photovoltaic materials. CZTSe films have been prepared using a single-step co-evaporation method at a relatively low temperature (i.e., below 500 °C). Due to the volatile nature of tin-selenide, the control over substrate temperature (i.e., growth temperature) is very important in terms of the deposition of high-quality CZTSe films. In this regard, the effects of growth temperatures on the CZTSe film morphology were investigated. The suitable temperature range to deposit CZTSe films with Cu-poor and Zn-rich compositions was 380–480 °C. As the temperature increased, the surface roughness of the CZTSe film decreased, which could improve p/n junction properties and associated device performances. Particularly, according to capacitance-voltage (C-V) and derived-level capacitance profiling (DLCP) measurements, the density of interfacial defects of CZTSe film grown at 480 °C showed the lowest value, of the order of ~3 × 1015 cm−3. Regardless of applied growth temperatures, the formation of a MoSe2 layer was rarely observed, since the growth temperature was not high enough to have a reaction between Mo back contact layers and CZTSe absorber layers. As a result, the photovoltaic (PV) device with CZTSe film grown at 480 °C yielded the best power conversion efficiency of 6.47%. It is evident that the control over film growth temperature is a critical factor for obtaining high-quality CZTSe film prepared by one-step process.

energies

Fabrication and Characterization of Cu2ZnSnSe4 Thin-Film Solar Cells using a Single-Stage Co-Evaporation Method: Effects of Film Growth Temperatures on Device Performances