English (United Kingdom)

https://curated-unify.zendy.io/wp-json/zendy-region/v1/featured_content/oa?rat=en

https://curated-unify.zendy.io/wp-json/zendy-region/v1/highlighted_journal/

Global: Zendy Plus annual

Presents the access of premium content as premium feature

Premium Content

Presents the keyphrase highlighting as premium feature

Keyphrase Highlighting

Presents the summarisation as premium feature

Summarisation

Insights

Presents the pdf analysis as premium feature

PDF Analysis

Presents the zaia usage as premium feature

ZAIA

Global: Zendy Plus monthly

Global: Zendy Tools annual

Global: Zendy Tools monthly

Global: Zendy Free Plan

A novel glass-ceramic coating was applied onto the 1Cr11Ni2W2MoV stainless steel. The oxidation and corrosion behaviors of coated and uncoated steels were comparatively investigated in air and in the presence of NaCl + Na2SO4 eutectic deposits at 650 °C, respectively. Protective scales formed on the surface of stainless steel prevented the severe oxidation of the alloy. Catastrophic hot corrosion occurred on the steel when a salt film was attached, producing loose iron oxide layers and internal corrosion zone. The glass-ceramic coating acted as a barrier that effectively hindered the invasion of corrosive species during the oxidation and hot corrosion tests.

Improved Oxidation and Hot Corrosion Resistance of 1Cr11Ni2W2MoV Stainless Steel at 650 °C by a Novel Glass-Ceramic Coating